Descrition:
Clear / Black 6061 Aluminum Porifle , Anodizeing Aluminium Construction System
Hentec Industry Company is an aluminum extrusion manufacturer .For over a decade , we have focused exclusively on producing a wide range of aluminum products , including curtain wall aluminum profile ,aluminum solar panel frame ,industry profile ,and more . Our constant efforts and focus on product improvement have helped us to make our products light , stable , durable ,corrosion resistant ,and easy to install .
| Item | Clear / Black Anodizeing Aluminum Construction System , 6063 - T5 / 6061 - T6 |
| Alloy | 6061,6060,6063,6005 etc |
| Temper | T4, T5, T6,T66 |
| Surface | oxidation,Oxidation coloring,Powder coating, Anodizing(clear, satin, bronze, black, golden, silver, other multicolor), Electrophoresis,PVDF coating, Mill finish, polished, color coated,Wire drawing,Wood grain,etc |
| Application | Construction ; Solar roof mounting system ; Aerospace; Ship; Armarium; Industrial equipment,etc |
| Technology Supports | 1,Engineering design
2,AutoCAD, pro/e ,UG drawing |
| Standard | Meet the China national standard and Europe standard and American standard. |
| Extrusion Tolerance | GB/T5237-2000 (Chinese Standard) |
| Machining Tolerance | GB/T 1804-92 |
| Standard for Anodizing | GB5237.2-2004 |
| Manufacturing Process | Die designing→ Die making→ Smelting& alloying→ Extruding→ Cutting→ CNC machining→ Driling→ Tapping→ Surface treatment→ Welding→ Assembling→ Packing |
| Packing method | 1. Standard packing: Eachprofile will be wrapped in the EPE sheet in order to protect the profiles' surfaces, kraft paper wrapped in bundles.
2. Special packing: wooden cases+iron trays.
3. Bundles or boxes with wooden bars
4. EPE+carton boxes.
5. Customized packing methods are welcomed.
6.13 tons to a 20 feet container, 20 tons to a 40 feet container |
Order,payment,terms,shipment
1, Minimum order: 500kg per trial order 1 piece of sample free of charge provided by approval and kept for future mass production.
2, Sample Lead Time: 25 working days(15 days for making the tool and 10 days making the samples. Before sending the samples to customer, samples should pass strict test in our lab. )Production Lead time: it depends on customers' order quantity ( 30 working days after deposit).
3, Payment: (Can negotiate with customers, our usual practices are as follow)
4, Tooling:100% prepaid by T/T.
5, Parts:30% upon order confirmation and balance before delivery by T/T
Applications:
Commercial center,hoptial ,school and airport,etc
Specifications:
1. Primary Technical Data
1) Chemical composition
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Impurity | Al |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest |
| 6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | - | 0.15 | 0.1 | 0.15 | Rest |
| 6005 | 0.6-0.9 | 0.35 | 0.1 | 0.1 | 0.40-0.6 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
2) Mechanical property
| Alloy | Temper | Tensile strength | Yield strength | Elongation |
| 6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% |
| T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% |
| 6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
3. Surface Treatment of Sections
| (Class) | (μm),not diminish than | acid-resistant | abrasion resistance |
| (Min-average film
thickness) | (Min-part film
thickness) | CASS | (S) | |
| (h) | Class | (f, g /μm) |
| AA10 | 10 | 8 | 16 | ≥9 | ≥50 | ≥300 |
| AA15 | 15 | 12 | 32 | ≥9 | ≥75 | ≥300 |
| AA20 | 20 | 16 | 56 | ≥9 | ≥100 | ≥300 |
| AA25 | 25 | 20 | 72 | ≥9 | ≥125 | ≥300 |
Competitive Advantage:
We focuses on the technological development, manufacture and trade of aluminum alloy products. We have 22 extrusion lines, 3 anodizing lines, 3 powder coating lines and 1 electrophoresis coating lines. Moreover, there are also more than 40 sets of processing machines, such as CNC, Milling Machine, Lathe, Drilling Machine and Punching Machine. Therefore, we have become an aluminum product production base for many famous companies both from domestic and overseas markets.